| UNS Number | N06075 |
| Werkstoff Number | 2.4951, 2.4630 |
| Standards | ASTM B637, RRMS 33030/1 (MSRR 7004), 7022, 7063, 7070, 7162, 7193, 7952, BS:HR 203, 3HR1, HR3, HR4, BS4HR 601 |
| Physical Property | British Units | Metric Units | ||
| Density | RT | 0.302 lb/in3 | RT | 8.37 g/cm3 |
| Melting Range | 2445-2515°F | - | 1340-1380°C | - |
| Electrical Resistivity | 400°F | 44.1 µohm-in | 200°C | 112µohm-cm |
| 800°F | 46.0 µohm-in | 400°C | 117 µohm-cm | |
| 1000°F | 45.5 µohm-in | 600°C | 115 µohm-cm | |
| 1200°F | 45.3 µohm-in | 700°C | 115 µohm-cm | |
| 1400°F | 45.3 µohm-in | 800°C | 115 µohm-cm | |
| 1600°F | 45.3 µohm-in | 900°C | 115 µohm-cm | |
| 1800°F | 45.6 µohm-in | 1000°C | 116 µohm-cm | |
| Thermal Conductivity | 800°F | 133 Btu-in/ft2-hr-°F | 400°C | 18.6 W/m-°C |
| 1000°F | 149 Btu-in/ft2-hr-°F | 600°C | 22.7 W/m-°C | |
| 1200°F | 164 Btu-in/ft2-hr-°F | 700°C | 24.7 W/m-°C | |
| 1400°F | 179 Btu-in/ft2-hr-°F | 800°C | 26.5 W/m-°C | |
| 1600°F | 193 Btu-in/ft2-hr-°F | 900°C | 28.4 W/m-°C | |
| 1800°F | 207 Btu-in/ft2-hr-°F | 1000°C | 30.1 W/m-°C | |
| Mean Coefficientof Thermal Expansion | 70-800°F | 7.9 µin/in -°F | 20-500°C | 14.3 µm/m-°C |
| 70-1000°F | 8.2 µin/in -°F | 20-600°C | 15.0 µm/m-°C | |
| 70-1200°F | 8.5 µin/in -°F | 20-700°C | 15.4 µm/m-°C | |
| 70-1400°F | 8.9 µin/in -°F | 20-800°C | 16.5 µm/m-°C | |
| 70-1600°F | 9.4 µin/in -°F | 20-900°C | 17.1 µm/m-°C | |
| 70-1800°F | 10.3 µin/in -°F | 20-1000°C | 18.2 µm/m-°C | |
| Dynamic Modulusof Elasticity | 70°F | 32.0 x 106 psi | 20°C | 221 GPa |
| 400°F | 30.5 x 106 psi | 200°C | 210 GPa | |
| 800°F | 28.2 x 106 psi | 400°C | 197 GPa | |
| 1000°F | 27.0 x 106 psi | 600°C | 181 GPa | |
| 1200°F | 25.5 x 106 psi | 700°C | 173 GPa | |
| 1400°F | 24.6 x 106 psi | 800°C | 165 GPa | |
| 1600°F | 22.6 x 106 psi | 900°C | 153 GPa | |
| 1800°F | 20.5 x 106 psi | 1000°C | 140 GPa | |
| Form | TestTemperature | 0.2% OffsetYield Strength | UltimateTensile Strength | Elongation | |||
| Sheet | °F | °C | ksi | MPa | ksi | MPa | % |
| RT | RT | 59.4 | 407 | 114.4 | 792 | 31 | |
| 1000 | 538 | 51.9 | 363 | 105.6 | 726 | 27 | |
| 1200 | 649 | 40.0 | 275 | 69.3 | 473 | 32 | |
| 1400 | 760 | 22.0 | 152 | 41.4 | 286 | 75 | |
| 1600 | 871 | 9.9 | 68 | 20.2 | 139 | 90 | |
| 1800 | 982 | 4.4 | 31 | 9.7 | 66 | 91 | |
| Nickel | 76 Balance |
| Cobalt | 1 max. |
| Chromium | 20 |
| Iron | 5 max |
| Titanium | 0.4 |
| Manganese | 1 max. |
| Silicon | 1 max. |
| Aluminum | 0.4 max. |
| Titanium | 0.4 |
| Carbon | 0.11 |
| Haynes75 available sizes and specifications | |
| Grade | Haynes75 |
| Nickel plate | Thickness: 0.3mm - 150.0mmWidth: 1000mm - 3000mm |
| Nickel strip/ nickel foil | Thickness: 0.02mm - 16.0mm Width: 5mm - 3000mm |
| Nickel coil | Thickness: 0.3mm - 16.0mm Width: 1000mm - 3000mm |
| Nickel pipe | Outside diameter: 6mm - 1219mm Thickness: 0.5mm - 100mm |
| Nickel Capillary Pipe | Outside diameter: 0.5mm - 6.0mm Thickness: 0.05mm - 2.0mm |
| Nickel bar | Diameter: Ф4mm - Ф600mm |
| Nickel wire rod | Diameter：Ф0.01mm - Ф6mm |